[1]王玲,吳浩,管學(xué)茂,等.應(yīng)力-化學(xué)介質(zhì)-凍融循環(huán)協(xié)同作用下水泥基材料失效機(jī)理及壽命預(yù)測(cè)的研究[J].中國材料進(jìn)展,2010,(9):025-33.
WANG Ling,WU Hao,GUAN Xuemao,et al.Research on Failure Mechanism and Service Life Prediction of High Performance Cementitious Materials under the Synergistic Effect of Stress,Chemical Medium and Freezing Thawing Cycle[J].MATERIALS CHINA,2010,(9):025-33.
點(diǎn)擊復(fù)制
應(yīng)力-化學(xué)介質(zhì)-凍融循環(huán)協(xié)同作用下水泥基材料失效機(jī)理及壽命預(yù)測(cè)的研究(
)
中國材料進(jìn)展[ISSN:1674-3962/CN:61-1473/TG]
- 卷:
-
- 期數(shù):
-
2010年第9期
- 頁碼:
-
025-33
- 欄目:
-
特約研究論文
- 出版日期:
-
2010-10-26
文章信息/Info
- Title:
-
Research on Failure Mechanism and Service Life Prediction of High Performance Cementitious Materials under the Synergistic Effect of Stress,Chemical Medium and Freezing Thawing Cycle
- 作者:
-
王玲; 吳浩; 管學(xué)茂; 黃鵬飛
-
中國建筑材料科學(xué)研究總院 綠色建筑材料國家重點(diǎn)實(shí)驗(yàn)室,北京 100024
- Author(s):
-
WANG Ling; WU Hao; GUAN Xuemao; HUANG Pengfei
-
State Key Laboratory of Green Building Materials,China Building Materials Academy,Beijing 100024,China
-
- 關(guān)鍵詞:
-
失效機(jī)理; 壽命預(yù)測(cè); 化學(xué)介質(zhì); 水泥基材料; 凍融循環(huán)
- 文獻(xiàn)標(biāo)志碼:
-
A
- 摘要:
-
針對(duì)水泥基材料在應(yīng)力-化學(xué)介質(zhì)-凍融循環(huán)協(xié)同作用下的耐久性進(jìn)行了研究,并開發(fā)了多種材料失效試驗(yàn)方法和裝置。砂漿試件應(yīng)力-化學(xué)腐蝕協(xié)同作用試驗(yàn)裝置的特點(diǎn)是加載穩(wěn)定,克服了應(yīng)力松弛;協(xié)同作用耐久性試驗(yàn)裝置可以用于監(jiān)測(cè)協(xié)同作用下鋼筋混凝土試件性能的衰減過程。研究發(fā)現(xiàn):礦物摻合料改善抗?jié)B性的能力依次是礦渣粉、活化煤矸石粉、粉煤灰;隨應(yīng)力比加大和凍融循環(huán)次數(shù)增加,水泥基材料中鋼筋銹蝕加速、化學(xué)介質(zhì)的滲透速度和深度增大,協(xié)同作用加速了水泥基材料的失效;可以用一元二次函數(shù)來近似預(yù)測(cè)氯鹽-凍融循環(huán)-彎曲荷載協(xié)同耦合作用下的壽命。
備注/Memo
- 備注/Memo:
-
收稿日期:2009-12-10
基金項(xiàng)目:973項(xiàng)目“高性能水泥制備和應(yīng)用的基礎(chǔ)研究”（2001CB610706）,“水泥低能耗制備與高效應(yīng)用的基礎(chǔ)研究”(2009CB623100)
通信作者:王〓玲,女,1968年生,教授級(jí)高工